SUZHOU HSF ELECTRONIC MATERIALS TECHNOLOGY CO., LTD.
Suzhou HSF Electronic Materials Technology Co., Ltd
Add to Cart
Clear PET 25micron, Fluorine Release, stable peeling force, high residual adhesion, solvent resistance, low iridescence.
| S/N | Item | Unit | Value | |
| 1 | Backing Film Type | Clear PET 25μm | ||
| 2 | Density | g/cm³ | 1.4 | |
| 3 | Thickness | μm | 25 | |
| 4 | Width | mm | 900-1300 | |
| 5 | Tensile Strength (ASTM D 882) | MD | Mpa | ＞200 |
| TD | ＞200 | |||
| 6 | Elongation @ break (ASTM D 882) | MD | % | ＞160 |
| TD | ＞110 | |||
| 7 | Heat Shrinkage (ASTM D 1204) | MD | % | ＜1.4 |
| TD | ＜0.3 | |||
| 8 | Release Force (PSTC) | gf/25mm | 5-10 | |
| 9 | Sub-sequent Adhesion Rate (PSTC) | % | ≥85 | |
Fluorine release film is made of PET as the base material and coated with fluorine release agent on one side.
It has the advantages of stable peeling force, high residual adhesion, solvent resistance, and low iridescence.
It is recommended to use this product for processing with dry or hot lamination process.
Be sure to evaluate the actual processing requirements (material/process) to confirm the suitability of this product before ordering.
High temperature/high humidity must be avoided, and more importantly, direct sunlight must be avoided.
UV light will affect the quality performance of the release film.