SUZHOU HSF ELECTRONIC MATERIALS TECHNOLOGY CO., LTD.
Suzhou HSF Electronic Materials Technology Co., Ltd
Add to Cart
PET Non-Silicone Release, High temperature resistant tape, silicone protective film, labels, cellphone.
| S/N | Test Item | Unit | Standard | Value | Test Method | ||
| 1 | Thickness | μm | 50 ±2% | 49.72 | GB/T6672 | ||
| 2 | Color | - | Blue | - | - | ||
| 3 | Tensile Strength | MD | Mpa | ≥180 | 187 | GB/T 1040.3 | |
| TD | Mpa | ≥190 | 196 | ||||
| 4 | Elasticity Modulus | MD | Mpa | / | 4144 | ||
| TD | Mpa | / | 4230 | ||||
| 5 | Elongation @ break (%) | MD
| % | ≤200 | 148 | ||
| TD | % | ≤200 | 139 | ||||
| 6 | Thermal Shrinkage | MD | % | ≤1.5 | 0.96 | 1 | 150℃/30min |
| TD | % | ≤0.0 | 0.00 | 0 | 200℃/10min | ||
| 7 | Friction Coefficient | F/M-US | % | ≤0.65 | 0.5 | GB/T 10006 | |
| F/M-UK | % | ≤0.50 | 0.3 | ||||
| 8 | Haze | % | ≤5 | 2.99 | GB/T2410 | ||
| 9 | Luminousness | % | ≥86 | 89.4 | GB/T2410 | ||
| 10 | Glossiness | % | ≥100 | 133 | GB/T8807 | ||
| 11 | Wetting Tension | mN/m | ≥50 | 58 | GB/T14216 | ||
| 12 | Release Force | gf/25mm | 3-5 | 4 | Final 10, 20min. | ||
| 13 | Sub-sequent Adhesion Rate | % | 91% | 92 | |||
It is applied to high temperature resistant tape, silicone protective film, labels, cellophane, etc.
It is suitable for the release, transfer lamination and processing of various adhesive materials for punching.
Product features:
1. PET is used as the substrate for precision coating of silicone-free release agent, forming a uniform and stable coating on the surface.
2. Class 1000 dust-free workshop, strict appearance management.
3. No silicon pollution.
4. Customized material thickness, color, etc. according to customer requirements.